Nickel 270 Properties Characteristic and Chemical Composition

Nickel 270/ UNS N02270/ ASTM F3 Properties Characteristic:

Nickel 270/ UNS N02270/ASTM F3/ W-Nr. 2.4050 is a high purity garde of nickel mad by power metallurgy, which has a low base hardness and high ductility. The extreme purity is useful for components of hydrogen thyratrons.

Chemical Composition of Nickel 270 Alloy

Nickel: ≥ 99.9

Copper: ≤0.01

Iron:  ≤0.05

Manganese: ≤0.003

Carbon: ≤0.02

Sulfur: ≤0.003

Titanium: ≤0.005

Magnesium: ≤0.005

Silicon: ≤0.005

Hastelloy G35 alloy Properties characteristic

Hastelloy G35 Alloy Properties characteristic

Hastelloy G35 Alloy Bar for Poland Client

Hastelloy G35 alloy is to provide corrosion resistance to the most difficult phosphoric acid enviroments. G35 alloy is much less susceptible to chloride-induced stress corrosion cracking than the stainless steels and nickel-chromium iron alloys traditionally used in"wet process" phosphoric acid. 

Due to its very high chromium content, G35 is extremely resistant to other oxidizing acids, such as nitric, and mixtures containing nitric acid. It possesses moderate resistance to reducing acids. Due to its appreciable molybdenum content, and unlike other nickel-chromium-molybdenum alloys, it's very resistant to "caustic de-alloying" in hot sodium hydroxide.

Hastelloy G30 alloy Properties characteristic, Heat treatment & Fabrication

Hastelloy G30 alloy:

Hastelloy G30 alloy Seamless pipes 6meter

Properties characteristic:

Hastelloy G30 alloy is a high chromium nickel base alloy shows superior corrosion resistance over most other nickel and iron base alloys in commercial phosphoric acid and many complex environments containing highly oxidizing agents such as nitric acid.

Heat Treatment & Fabrication:

The annealing temperature for HASTELLOY G30 alloy is 1177℃（2150℉),and water quenching is advised(rapid air cooling is feasible with structures thinner than 10mm(0.375in). A hold time at the annealing temperature of 10 to 30 minutes is recommended, depending on the thickness of the structure(thicker structures need the full 30 minutes).

Hastelloy G30 alloy can be hot forged, hot rolled, hot upset, hot extruded, and hot formed. And it can apply in wire, sheet, plate, scrip, bar, Welded pipes& seamless pipes, forged. 

Hastelloy B3/Alloy B3 Property Characteristic, Fabrication & Heat treatment

Hastelloy B3/ Alloy B3 Property Characteristic

B3 alloy Seamless pipe 5.8 meter for England Client

Hastelloy B3 has extremely high resistance to the hydrochloric acid, sulfuric, acetic, formic and phosphotic acids, and other non-oxidizing media. And it has excellent resistance to pitting corrosion, to stress-corrosion cracking and to knife-line and heat-affected zone attack.

Fabrication & Heat treatment for Hastelloy B3

Wrought products of B3 alloy are supplied in the Mill Annealed condition, unless otherwise specified. This solution annealing procedure has been designed to optimize the alloy's corrosion resistance and ductility. Following all hot forming operations, the material should be re-annealed, to restore optimum properties. The alloy should also be re-annealed after any cold forming operations that result in an outer fiber elongation of 7% or more. The annealing temperature for b3 alloy is 1066℃（1950℉），and water quenching is advised(rapid air cooling is feasible with structures thinner than 10mm(0.375in.). A hold time at the annealing temperature of 10 to 30 minutes is recommended, depending on the thickness of the structure(thicker structures need the full 30 minutes).

Hastelloy b3 can be hot forged, hot rolled, hot upset, hot extruded, and hot formed. The B3 alloy more sensitive to strain and strain rates than the austenitic stainless steels, and the hot working temperature range is quite narrow. The alloy is stiffer than most austenitic stainless steels, and more energy is required during cold forming. Also, the hastelloy b3 work hardens more readily than most austenitic stainless steels, and may require several stages of cold work, with intermediate anneals.

Hastelloy B2/ Alloy B2 Fabrication and Heat treatment, Corrosion Resistance

Alloy B2 

Alloy B2 Seamless pipe 6m*4in. for Poland Client

Alloy B2 Fabrication and Heat treatment:

Welding Alloy B2 can be performed by TIG, MIG as well as coated electrode. Dissmilar metal welding alloy b2 to alloy b3 is possible using AWS ERNiMo-10 for GTAW and GMAW operations and ENiMo-10 for SMAW welding. The work piece should be thoroughly cleaned with acetone or other suitable cleaners to insure that all contaminants and markings are removed. Grinding prior to welding can be performed with a clean alumina-wheel that has not been previously used on any iron-based materials. There is no need for pre or post heat treatment processes unless the work piece has been formed by any means. A full solution anneal before welding is required on pieces that have been formed. Cold-formed pieces must be shot-peened before annealing.

Hot working should be performed in a temperature range between 1700℉ to 2250℉ with heavy deformation performed toward the upper end of the range. Reheating of the work piece may be necessary. A full solution anneal should be performed on all hot-worked pieces and any cold-worked pieces with more than 15% deformation followed by a water quench.

Solution annealing of Alloy b2 is performed at 1950℉ for 10 minutes at temperature followed by a water quench. Subject material should be charged into a hot furnace and monitored closely for accurate time at temperature. Contact thermocouples are preferred.

Resistance of Corrosion for Alloy B2:

The high molybdenum content in Alloy b2 gives the alloy excellent resistance to hydrochloric acid over a wide range of concentrations and temperatures.

B2 also shows good resistance to hydrogen chloride, sulfuric acid and phosphoric acids and has excellent resistant to pitting and stress corrosion cracking in the heat-affected zone. Uniform corrosion rates in various environments is very similar compared to the other Ni-Mo alloys such as B3. The presence of any oxidizing media, even in trace amounts, will significantly increase corrosion. B2 should not be used in oxidizing media, as these alloys show little to no resistance in such environments.

Alloy B2/Hastelloy B2/UNS N10665/W.Nr. 2.4617 Properties and application notes

Hastelloy B2 Characteristic Properties and application notes

Alloy B2,Hastelloy B2,UNS N10665, W.Nr. 2.4617 Wire 20m*0.5mm

Hastelloy B2 Properties and Notes:

Hastelloy B2 / UNS N10665/ W.Nr. 2.4617 is a solid solution strengthened, nickel-molybdenum alloy, typically used in extreme reducing conditions. B2 has significantly low carbon, silicon and iron compared to its' predecessor, Alloy B(UNS N10001), making the alloy less susceptible to decreased corrosion resistance in the weld zone, in the as-welded condition. Controlling other alloying elements such as iron and chromium solved other issues concerning fabricability. Stringent chemistry control along with years of development has resulted in the alloy used now, both in alloy B2 and alloy B3. now, alloy B2 with restricted chemistry can be used in the welded condition and is less susceptible to SCC under many conditions. As always, care must taken in selecting the right alloy for the desired application.

Hastelloy B2 should not be used at temperatures between 1000℉ and 1600℉ as the alloy forms secondary phases that could decrease the ductility of the material. 

Hastelloy C2000 alloy features and applications

The Applications And Features of Hastelloy C2000/UNS N06200

The features of Hastelloy C2000 alloy:

Hastelloy C2000 alloy/UNS N06200 is unique among the versatile nickel-chromium-molybdenum materials in having a deliberate copper addition. This provides greatly enhanced to oxidizing chemicals and process streams contaminated with ferric ions and dissolved oxygen.

Like other nickel alloys, it is ductile, easy to form and weld, and possesses exceptional resistance to stress corrosion cracking in chloride-bearing solutions(a form of degradation to which the austenitic stainless steels are prone). It is able to withstand a wide range of oxidizing and non-oxidizing chemicals, and exhibits outstanding resistance to pitting and crevice attack in the presence of chlorides and other halides.

Hastelloy c2000 applications include reactors and heat exchangers.