The Mechanical Properties comparison between Nickel 200 and Nickel 201

Nominal Mechanical Properties of Nickel 200

Form	Tensile Strength		Yield Strength (0.2% Offset)		Elongation in 2 in. (51mm),  %	Hardness
	ksi	Mpa	ksi	Mpa		Brinell(3000 kg)	Rockwell B
Rod and Bar
Hot- Finished	60-85	415-585	15-45	105-310	55-35	90-150	45-80
Cold-Drawn	65-110	450-760	40-100	275-690	35-10	140-230	75-98
Cold-Drawn, Annealed or Hot-finished, Annealed	55-75	380-520	15-30	105-210	55-40	90-120	45-70
Plate
Hot-Rolled	55-100	380-690	20-80	140-550	55-35	100-150	55-80
Hot-Rolled, Annealed	55-80	380-550	15-40	105-275	60-40	90-140	45-75
Sheet
Hard	90-115	620-795	70-105	480-725	15-2	-	90min
Annealed	55-75	380-520	15-30	105-210	55-40	-	70max
Strip
Spring	90-130	620-895	70-115	480-795	15-2	-	95min
Annealed	55-75	380-520	15-30	105-210	55-40	-	64max
Tubing
Stress-Relieved	65-110	450-760	40-90	275-620	35-15	-	75-98
Annealed	55-75	380-520	12-30	85-210	60-40	-	70max
Condenser and Evaporator Tubing
Annealed	55-75	380-520	15-30	105-210	60-40	-	65max
Stress-Relieved	65-110	450-760	40-90	275-620	35-20	-	75-98
Wire, Cold-Drawn
Annealed	55-85	380-580	15-50	105-345	50-30	-	-
No. 1 Temper	70-95	485-655	40-75	275-520	40-20	-	-
Spring Temper	125-145	860-1000	105-135	725-930	15-2	-	-

Nominal Mechanical Properties of Nickel 201

Form	Tensile Strength		Yield Strength (0.2% Offset)		Elongation in 2 in. (51mm),  %	Hardness
	ksi	Mpa	ksi	Mpa		Brinell	Rockwell B
Rod and Bar
Hot- Finished and Hot-Finished, Annealed	50-60	345-415	10-25	70-170	60-40	75-100	-
Cold-Drawn	60-100	415-690	35-90	240-620	35-10	125-200	-
Cold-Drawn, Annealed	50-60	345-415	10-25	70-170	60-40	75-100	-
Plate
Hot-Rolled	50-70	345-485	12-35	83-240	60-35	-	-
Hot-Rolled, Annealed	50-70	345-485	12-35	83-240	60-40	-	-
Tubing and Pipe (Seamless)
Cold-Drawn, Annealed	50-70	345-485	10-28	70-195	60-40	-	62max.
Stress-Relieved	60-105	415-725	30-85	205-585	35-15	-	70-95